ELEMENT Z  - Zircon Blanks   

 

• Yttria-stabilized zirconia (ZrO2) with Aluminium oxide (AI2O3)

• Fine grain size for smooth surfaces

• High quality and resistance

• Isostatic pressing manufacturing

• After sintering, they are extremely resistant to breakage or cracks

• High biocompatibility

• Precision during sintering

• Easy and roughless milling

 

 

Different esthetic qualities

CLASSIC

 

Classic quality is recommended to realise frameworks, bridges and copings for application of ceramic. It offers a sufficient opacity in order to cover the metallic post and core or those which are naturally colored.

 

Not recommended to realise full anatomic crowns.

Blanks are available in white - opaque or the range of B-colours.

 

 

Composition

 

ZrO2 + HfO2 + Y2A3:  ≥   99,0%     

Y2A3:      4,5-6,0%

HfO2:    1,8-2,2%  

Al2O3:    0,24-0,26%     

 

 

 

Technical Data

Grain size                                 <0,4µ
Flexural strength (3 point)     1.200 MPa
Flexural strength (4 point)     1.100 MPa
CTE                                             11,0
Density                                      6,05g/cm³
E-Module                                   210 GPa
Vickers hardness                      1.250

TRANSLUCENT

 

Translucent quality shows esthetic translucency with high density and strength. This quality allows you to realise the entire and complete reconstruction of full anatomic zircon as well as using with the add on technique.

The high flexural strength offers great advantages in the side area. Translucent zircone is very similar in its surface finish to natural teeth.

Because of the addition of rare earths, which are already mixed with the base material, the colouring goes homogeneous throughout the blank.

The blanks are available in white - translucent or precoloured in a wide range from A1 - D3.

Composition

ZrO2 + HfO2 + Y2A3:  ≥   99,0%     

Y2A3:      4,5-6,0%

HfO2:    1,8-2,2%  

Al2O3:    0,03-0,07%   

 

Technical Data

 

Grain size                                 <0,4µ

Flexural strength (3 point)     1.200 MPa

Flexural strength (4 point)     1.100 MPa

CTE                                             10,7

Density                                      6,07g/cm³

E-Module                                   210 GPa

Vickers hardness                      1.250

SHINE HT

SHINE HT is a high-translucent quality which is specially adapted to realize the anterior teeth. The brilliant and natural colouring is one of the major advantages.

SHINE offers a much more high strength than lithium disilicate or other glas ceramics.

The natural esthetic of this quality allows a variety of dental care reconstructions.

This quality is recommended for crowns, inlays, Veneers, Onlays and bridges up to 3 elements.

The improved optic combined with the proven properties of zircone  - ideal milling characteristics, aging resistance, strength and biocompatibility - makes SHINE HT a great solution for dental restorations, especially in the front area.

SHINE HT is available in white-high translucent as well as precoloured in different colours from A1-C2.

 

 

 

Composition

ZrO2 + HfO2 + Y2A3:  ≥   99,0%     

Y2A3:      8,5-9,5%

HfO2:    1,8-2,2%  

Al2O3:    0,04-0,06% 

 

 

Technical Data

  

Grain size                                 <0,6µ

Flexural strength (3 point)     840 MPa

Flexural strength (4 point)     680 MPa

CTE                                             10,4

Density                                      6,04g/cm³

E-Module                                   210 GPa

Vickers hardness                      1.250

BRIGHT

 

The new BRIGHT quality is translucent and offers a high strength in the same time. Because of its unique combination of translucency (min. 54%), esthetic and strength this quality is specially convenient for all dental reconstructions such as crowns and bridges, inlays and onlays, Veneers in frontal and side area. The BRIGHT quality is suitable for a multiplicity of modern functional and esthetic requirements.

Especially for wide-ranged reconstructions in the anterior area the advantages of BRIGHT offer a new dimension of solutions. This construction can be designed full-anatomically or for the using of the add on technique.
 

BRIGHT quality is available in white-translucent as well as precoloured in different colours from A1- D3.

 

Composition

 

ZrO2 + HfO2 + Y2A3:  ≥   99,0%     

Y2A3:      6,5-7,5%

HfO2:    1,8-2,2%  

Al2O3:    0,04-0,06% 

 

 

Technical Data

 

Grain size                                 <0,5µ

Flexural strength (3 point)     1.100 MPa

Flexural strength (4 point)     860 MPa

CTE                                             10,6

Density                                      6,06g/cm³

E-Module                                   210 GPa

Vickers hardness                      1.250


 

ELEMENT - Wax Blanks   

 

• burn-out wax composition for CAD CAM technology

• recommended for the milling of inlays, onlays, single crowns as well as for bridges

• to be used with casting or pressing technology

• temperature stable wax which does not grease

WAX BLANKS

 

• pleasant colors for detailed aesthetics

• excellent and stable contours

smooth surfaces after milling

• Ø 98,5mm, 95mm and suitable for Amann Girrbach system

14mm & 20mm height

 

 

 

 

 

 

ELEMENT P - PMMA Blanks   

 

• PMMA for the production of single crowns and large bridges

• for temporary restorations

• burnable PMMA, can be used for traditional casting

 

PMMA BLANKS

 

• Suitable for the production of temporary crowns and bridges

  for both casting and press technique

• Cost efficient milling of trial elements

• Free of any distortion

• Burns without residues

• Can be used to control the insertion in the patient’s mouth

  before making the final restauration

• excellent milling characteristics

• available in different shades

• Ø 98,5mm & 95mm

• different height

 

 

 

Dentify GmbH

Scheffelstr. 22

78234 Engen / Germany

info@dentify-gmbh.com

  • Wix Facebook page